PMMA AM700Z（Ultraviolet penetration）
PRODUCT DETAILS
PMMA AM700Z (Ultraviolet Penetration)
PMMA AM700Z is a specialized ultraviolet-transmitting acrylic material designed for optical and photochemical applications. It features high stiffness, strong mechanical integrity, and selective UV penetration with excellent surface quality. The following table presents its typical performance indicators.
Typical Indicators
| Category | Property | Test Standard / Condition | Unit | Value |
|---|---|---|---|---|
| Physical | Specific Gravity | GB/T 1033 | g/cm³ | 1.186 |
| Physical | Melt Index (230℃ / 3.8kg) | GB/T 3682 | g/10min | 2.4 |
| Mechanical | Tensile Strength (10mm/min) | GB/T 1040 | MPa | 85 |
| Mechanical | Elongation at Break (10mm/min) | GB/T 6344 | % | 3 |
| Mechanical | Flexural Strength (2mm/min) | GB/T 9341 | MPa | 136 |
| Mechanical | Flexural Modulus (2mm/min) | GB/T 9341 | MPa | 3860 |
| Impact | Izod Impact Strength (Notched, 1/8") | GB/T 1843 | KJ/m² | 2 |
| Optical | Light Transmittance (3mm) | GB/T 2410 | % | 54 |
| Optical | Haze (3mm) | GB/T 2410 | % | 91.6 |
| Flammability | Fire Rating | GB/T 2048 | — | HB |
Recommended Injection Molding Conditions
- Pre-drying Temperature: 60–80 °C
- Pre-drying Time: 3–4 hours
- Melting Temperature: 210–240 °C
- Mold Temperature: 50–70 °C
Note: The values above are for reference only. Users must test the material under their own processing conditions to confirm suitability for specific applications and performance standards.