PC GF2010R
PRODUCT DETAILS
PC GF2010R (Fireproof) Material Data
PC GF2010R is a fireproof polycarbonate reinforced with fiberglass, offering excellent mechanical strength, thermal resistance, and dimensional stability. With UL94 V0 fire rating and superior impact strength, it is widely used in automotive, electrical housings, and industrial applications requiring safety and durability.
Key Features
- UL94 V0 fire rating for superior flame resistance
- Reinforced with 9.5% fiberglass for high strength
- Excellent tensile and flexural properties
- High heat deflection temperature (136℃)
- Good impact resistance and dimensional stability
Typical Properties
| Property | Test Standard | Condition | Unit | GF2010R |
|---|---|---|---|---|
| Specific Gravity | ASTM D792 | — | g/cm³ | 1.26 |
| Melt Index | ASTM D1238 | 300℃ / 1.2kg | g/10min | 15.4 |
| Tensile Strength | ASTM D638 | 20 mm/min | MPa | 81 |
| Elongation at Break | ASTM D638 | 20 mm/min | % | 6.4 |
| Flexural Strength | ASTM D790 | 2 mm/min | MPa | 128 |
| Flexural Modulus | ASTM D790 | 2 mm/min | MPa | 3527 |
| Izod Impact Strength | ASTM D256 | 1/8 inch | kJ/m² | 13 |
| Heat Deflection Temp. | ASTM D648 | 1.8 MPa | ℃ | 136 |
| Fire Rating | UL-94 | 1.6 mm | Class | V0 |
| Fiberglass Content | High-temp combustion furnace | — | % | 9.5 |
Injection Molding Recommendations
- Pre-drying Temperature: 120 ℃
- Pre-drying Time: 3–4 hours
- Melting Temperature: 270–290 ℃
Disclaimer
The property data listed are typical values for reference only. They are not guaranteed specifications and should not be used as inspection criteria. Users must evaluate the material under their own processing conditions to confirm suitability for intended applications. Responsibility for end-use performance lies solely with the user.
Source: Su Master New Materials (Guangdong) Co., Ltd. — Technical Data Sheet (GF2010R):contentReference[oaicite:1]{index=1}.