PETG SDT90G
PRODUCT DETAILS
SDT90G Material Performance Description
SDT90G is a high-transparency engineering material developed by Su Master New Materials (Guangdong) Co., Ltd.. It offers excellent clarity, strong impact resistance, and balanced rigidity, making it suitable for injection molding applications that require toughness, transparency, and stable dimensional performance.
✅ Key Physical, Mechanical & Optical Properties
| Property | Test Standard | Condition | Unit | SDT90G |
|---|---|---|---|---|
| Specific Gravity | GB/T 1033 | — | g/cm³ | 1.25 |
| Melt Index | GB/T 3682 | 230℃ / 3.8kg | g/10min | / |
| Tensile Strength | GB/T 1040 | 10mm/min | MPa | 54 |
| Elongation at Break | GB/T 6344 | 10mm/min | % | / |
| Flexural Strength | GB/T 9341 | 2mm/min | MPa | 66 |
| Flexural Modulus | GB/T 9341 | 2mm/min | MPa | 1790 |
| Izod Impact Strength (Notched) | GB/T 1843 | 1/8 inch | KJ/㎡ | 93 |
| Light Transmittance | GB/T 2410 | 3mm | T(C) | 90 |
| Haze | GB/T 2410 | 3mm | H(C) | 1 |
| Heat Deflection Temperature | GB/T 1634 | 1.8MPa | ℃ | 68 |
| Fire Rating | GB/T 2048 | mm / 1.5min | — | HB |
✅ Recommended Injection Molding Conditions
- Pre-drying Temperature: /
- Pre-drying Time: /
- Melting Temperature: /
- Mold Temperature: /
Note: All technical indicators and data above are provided for reference only and are not guaranteed values. Users must verify material suitability based on actual processing and application requirements.