ABS ABS SD417S
PRODUCT DETAILS
ABS SD417S Material Performance Description
ABS SD417S is a high-strength ABS material produced by Su Master New Materials (Guangdong) Co., Ltd.. It provides excellent rigidity, superior impact resistance, and stable thermal performance, making it suitable for injection molding applications requiring strong toughness and durability.
✅ Key Physical, Mechanical & Thermal Properties
| Property | Test Standard | Condition | Unit | ABS SD417S |
|---|---|---|---|---|
| Specific Gravity | ASTM D792 | — | g/cm³ | 1.04 |
| Melt Flow Index | ASTM D1238 | 220℃ / 10kg | g/10min | 19.5 |
| Rockwell Hardness (R) | ASTM D785 | — | — | 111 |
| Tensile Strength (Yield) | ASTM D638 | 50mm/min, 3.2mm | MPa | 47.3 |
| Bending Strength | ASTM D790 | 2mm/min, 3.2mm | MPa | 64.9 |
| Flexural Modulus | ASTM D790 | 2mm/min, 3.2mm | MPa | 2230 |
| Notched Izod Impact | ASTM D256 | 23℃, 3.2mm | J/m | 208 |
| Heat Deflection Temperature | ASTM D648 | — | ℃ | 75 |
| Fire Rating | UL94 | 1.6mm | — | HB |
✅ Recommended Injection Molding Conditions
- Pre-drying Temperature: 70–80℃
- Pre-drying Time: 2–4 hours
- Melting Temperature: 190–230℃
- Mold Temperature: 40–70℃
Note: All technical indicators and data above are for reference only and not guaranteed values. Users must verify suitability based on actual application and processing requirements.