ABS SD181S
PRODUCT DETAILS
ABS SD181S Material Performance Description
ABS SD181S is a high-flow, general-purpose ABS material produced by Su Master New Materials (Guangdong) Co., Ltd.. With excellent fluidity, balanced mechanical properties, and stable dimensional performance, it is suitable for injection molding applications requiring high processing efficiency, rigidity, and durability.
✅ Key Physical, Mechanical & Processing Properties
| Property | Test Standard | Condition | Unit | ABS SD181S |
|---|---|---|---|---|
| Specific Gravity | ASTM D792 | — | g/cm³ | 1.04 |
| Shrinkage Rate | ASTM D955 | — | % | 0.4–0.7 |
| Melt Flow Index | ASTM D1238 | 220℃ / 10kg | g/10min | 42 |
| Rockwell Hardness (R) | ASTM D785 | — | — | 105 |
| Tensile Strength (Yield) | ASTM D638 | 50mm/min, 3.2mm | kg/cm² | 420 |
| Flexural Elongation | ASTM D638 | 50mm/min, 3.2mm | % | 10 |
| Bending Strength | ASTM D790 | 10mm/min, 6.4mm | kg/cm² | 610 |
| Bending Modulus | ASTM D790 | 10mm/min, 6.4mm | kg/cm² | 22900 |
| Notched Izod Impact | ASTM D256 | 23℃, 6.4mm | kg·cm/cm | 26 |
| Fire Rating | UL94 | 1.6mm | — | HB |
✅ Recommended Injection Molding Conditions
- Pre-drying Temperature: 70–80℃
- Pre-drying Time: 2–4 hours
- Melting Temperature: 190–240℃
- Mold Temperature: 40–70℃
Note: All technical indicators are for reference only and not guaranteed values. Users must confirm the material’s suitability based on their specific application and processing requirements.