ABS SD920S
PRODUCT DETAILS
ABS SD920S Material Performance Description
ABS SD920S is a high-rigidity, high-strength ABS material developed by Su Master New Materials (Guangdong) Co., Ltd.. With excellent tensile modulus, strong mechanical stability, and reliable heat resistance, this grade is suitable for injection molding applications requiring durability, dimensional stability, and robust performance.
✅ Key Physical, Mechanical & Thermal Properties
| Property | Test Standard | Test Condition | Unit | ABS SD920S |
|---|---|---|---|---|
| Specific Gravity | ISO 1183 | — | g/cm³ | 1.040 |
| Ball Indentation Hardness | ISO 2039 | — | N/mm² | 105 |
| Tensile Modulus (Flow) | ISO 527 | — | MPa | 2500 |
| Tensile Strength (Yield) | ISO 527 | 23℃ | MPa | 50 |
| Bending Strength | ISO 180 | 23℃ | MPa | 70 |
| Bending Modulus | ISO 180 | 23℃ | MPa | 2400 |
| Cantilever Beam Notched Impact | Internal Method | 6.4mm, 23℃ | KJ/㎡ | 16 |
| Heat Deflection Temperature | ISO 75 | 1.8MPa | ℃ | 93 |
✅ Recommended Injection Molding Conditions
- Pre-drying Temperature: 70–80℃
- Pre-drying Time: 2–4 hours
- Melting Temperature: 190–240℃
- Mold Temperature: 40–70℃
Note: All technical indicators above are for reference only and shall not be regarded as guaranteed values. Users must verify suitability based on actual processing and application requirements.