PA6 SDG15A-NC
PRODUCT DETAILS
PA6 SDG15A-NC Material Performance Description
PA6 SDG15A-NC is a high-performance polyamide 6 (nylon 6) material reinforced with 15% glass fiber, developed by Su Master New Materials (Guangdong) Co., Ltd.. It offers outstanding strength, rigidity, heat resistance, and dimensional stability, making it ideal for structural and engineering components requiring durability and mechanical reliability.
✅ Key Physical, Mechanical & Thermal Properties
| Property | Test Standard | Condition | Unit | PA6 SDG15A-NC |
|---|---|---|---|---|
| Specific Gravity | GB/T 1033 | — | g/cm³ | 1.235 |
| Melt Index | GB/T 3682 | 275℃ / 3.8kg | g/10min | 30 |
| Tensile Strength | GB/T 1040 | 10mm/min | MPa | 106 |
| Elongation at Break | GB/T 6344 | 10mm/min | % | 15 |
| Flexural Strength | GB/T 9341 | 2mm/min | MPa | 145 |
| Flexural Modulus | GB/T 9341 | 2mm/min | MPa | 5096 |
| Izod Impact Strength (Notched) | GB/T 1843 | 3.2mm, 23℃ | KJ/㎡ | 22.8 |
| Heat Deflection Temperature | GB/T 1634 | 1.8MPa | ℃ | 175 |
| Fire Rating | GB/T 2048 | mm / 1.5 min | — | HB |
✅ Recommended Injection Molding Conditions
- Pre-drying Temperature: 90–100℃
- Pre-drying Time: 4–6 hours
- Melting Temperature: 250℃
- Mold Temperature: 80–100℃
Note: All technical data and indicators above are for reference only and shall not be used as inspection or guaranteed values. Users must confirm material suitability according to their specific application and processing requirements.