PA6 SDG20A-NC
PRODUCT DETAILS
PA6 SDG20A-NC Material Performance Description
PA6 SDG20A-NC is a high-strength, 20% glass fiber reinforced polyamide 6 (nylon 6) compound produced by Su Master New Materials (Guangdong) Co., Ltd.. This grade features excellent mechanical strength, high rigidity, outstanding heat resistance, and superior dimensional stability, making it ideal for structural and engineering components in demanding industrial applications.
✅ Key Physical, Mechanical & Thermal Properties
| Property | Test Standard | Condition | Unit | PA6 SDG20A-NC |
|---|---|---|---|---|
| Specific Gravity | GB/T 1033 | — | g/cm³ | 1.29 |
| Melt Index | GB/T 3682 | 275℃ / 3.8kg | g/10min | 30 |
| Tensile Strength | GB/T 1040 | 10mm/min | MPa | 135 |
| Elongation at Break | GB/T 6344 | 10mm/min | % | 14.5 |
| Flexural Strength | GB/T 9341 | 2mm/min | MPa | 200 |
| Flexural Modulus | GB/T 9341 | 2mm/min | MPa | 6924 |
| Izod Impact Strength (Notched) | GB/T 1843 | 3.2mm, 23℃ | KJ/㎡ | 15.6 |
| Heat Deflection Temperature | GB/T 1634 | 1.8MPa | ℃ | 175 |
| Fire Rating | GB/T 2048 | mm / 1.5 min | — | HB |
✅ Recommended Injection Molding Conditions
- Pre-drying Temperature: 90–100℃
- Pre-drying Time: 4–6 hours
- Melting Temperature: 250℃
- Mold Temperature: 80–100℃
Note: All physical property indicators and data above are for reference only and shall not be regarded as guaranteed values. Users must verify material suitability according to their actual processing and application requirements.