111
PA6 SDG35A-NC
PRODUCT DETAILS
PA6 SDG35A-NC Material Performance Description
PA6 SDG35A-NC is a 35% glass fiber reinforced polyamide 6 (nylon 6) engineering material developed by Su Master New Materials (Guangdong) Co., Ltd.. This grade delivers extremely high rigidity, excellent heat resistance, strong structural strength, and outstanding dimensional stability—making it suitable for heavy-duty industrial and mechanical applications requiring maximum durability and performance.
✅ Key Physical, Mechanical & Thermal Properties
| Property | Test Standard | Condition | Unit | PA6 SDG35A-NC |
|---|---|---|---|---|
| Specific Gravity | GB/T 1033 | — | g/cm³ | 1.46 |
| Melt Index | GB/T 3682 | 275℃ / 3.8kg | g/10min | 32 |
| Tensile Strength | GB/T 1040 | 10mm/min | MPa | 125 |
| Elongation at Break | GB/T 6344 | 10mm/min | % | 12 |
| Flexural Strength | GB/T 9341 | 2mm/min | MPa | 178 |
| Flexural Modulus | GB/T 9341 | 2mm/min | MPa | 8750 |
| Izod Impact Strength (Notched) | GB/T 1843 | 3.2mm, 23℃ | KJ/㎡ | 15.5 |
| Heat Deflection Temperature | GB/T 1634 | 1.8MPa | ℃ | 210 |
| Fire Rating | GB/T 2048 | mm / 1.5 min | — | HB |
✅ Recommended Injection Molding Conditions
- Pre-drying Temperature: 90℃
- Pre-drying Time: 4–6 hours
- Melting Temperature: 250℃
- Mold Temperature: 90℃
Note: All physical and technical indicators above are for reference only and are not guaranteed values. Users must verify suitability according to their actual application and processing requirements.