PC+ABS SD3016H
PRODUCT DETAILS
SD3016H Material Performance Description
SD3016H is a high-quality engineering material manufactured by Su Master New Materials (Guangdong) Co., Ltd.. With excellent mechanical strength, strong impact resistance, and reliable V0 flame retardancy, it is ideal for injection molding applications that require durability, safety, and stable processing performance.
✅ Key Physical & Mechanical Properties
| Property | Test Standard | Condition | Unit | SD3016H |
|---|---|---|---|---|
| Specific Gravity | GB/T 1033 | — | g/cm³ | 1.18 |
| Melt Index | GB/T 3682 | 230℃ / 3.8kg | g/10min | 21 |
| Tensile Strength | GB/T 1040 | 10mm/min | MPa | 55 |
| Elongation at Break | GB/T 6344 | 10mm/min | % | 50 |
| Flexural Strength | GB/T 9341 | 2mm/min | MPa | 88 |
| Flexural Modulus | GB/T 9341 | 2mm/min | MPa | 2100 |
| Izod Impact Strength (Notched) | GB/T 1843 | 1/8 inch | KJ/㎡ | 60 |
| Heat Deflection Temperature | GB/T 1634 | 1.8MPa | ℃ | 88 |
| Flame Rating | GB/T 2048 | mm / 1.5 min | — | V0 |
✅ Recommended Injection Molding Conditions
- Pre-drying Temperature: 80–90℃
- Pre-drying Time: 3 hours
- Melting Temperature: 260℃
- Mold Temperature: 80℃
Note: The technical indicators listed above are for reference only and do not constitute guaranteed values. Users must independently verify suitability for their specific processing and application needs.