PC+ABS SD3100H
PRODUCT DETAILS
SD3100H Material Performance Description
SD3100H is a high-strength engineering material developed by Su Master New Materials (Guangdong) Co., Ltd.. Featuring excellent tensile performance, strong flexural strength, and reliable V0 flame retardancy, it is suitable for injection molding applications that require high rigidity, durability, and enhanced safety.
✅ Key Physical & Mechanical Properties
| Property | Test Standard | Condition | Unit | SD3100H |
|---|---|---|---|---|
| Specific Gravity | GB/T 1033 | — | g/cm³ | 1.18 |
| Melt Index | GB/T 3682 | 230℃ / 3.8kg | g/10min | 25 |
| Tensile Strength | GB/T 1040 | 10mm/min | MPa | 60 |
| Elongation at Break | GB/T 6344 | 10mm/min | % | / |
| Flexural Strength | GB/T 9341 | 2mm/min | MPa | 94 |
| Flexural Modulus | GB/T 9341 | 2mm/min | MPa | 2438 |
| Izod Impact Strength (Notched) | GB/T 1843 | 1/8 inch | KJ/㎡ | 44 |
| Heat Deflection Temperature | GB/T 1634 | 1.8MPa | ℃ | 90 |
| Flame Rating | GB/T 2048 | mm / 1.5 min | — | V0 |
✅ Recommended Injection Molding Conditions
- Pre-drying Temperature: /
- Pre-drying Time: /
- Melting Temperature: /
- Mold Temperature: /
Note: The technical data above are provided for reference only and should not be treated as guaranteed values. Users must confirm material suitability for their specific processing and application requirements.