SD2008G is a high-transparency engineering material manufactured by Su Master New Materials (Guangdong) Co., Ltd.. It offers excellent optical clarity, balanced mechanical strength, and stable thermal properties, making it suitable for injection molding applications that require transparency, toughness, and dimensional stability.
✅ Key Physical, Mechanical & Optical Properties
| Property | Test Standard | Condition | Unit | SD2008G |
|---|---|---|---|---|
| Specific Gravity | GB/T 1033 | — | g/cm³ | 1.27 |
| Melt Index | GB/T 3682 | 230℃ / 3.8kg | g/10min | / |
| Tensile Strength | GB/T 1040 | 10mm/min | MPa | 49 |
| Elongation at Break | GB/T 6344 | 10mm/min | % | / |
| Flexural Strength | GB/T 9341 | 2mm/min | MPa | 67 |
| Flexural Modulus | GB/T 9341 | 2mm/min | MPa | 1920 |
| Izod Impact Strength (Notched) | GB/T 1843 | 1/8 inch | KJ/㎡ | 8.8 |
| Light Transmittance | GB/T 2410 | 3mm | T(C) | 90 |
| Haze | GB/T 2410 | 3mm | H(C) | 1 |
| Heat Deflection Temperature | GB/T 1634 | 1.8MPa | ℃ | 64 |
| Fire Rating | GB/T 2048 | mm / 1.5min | — | / |
✅ Recommended Injection Molding Conditions
- Pre-drying Temperature: /
- Pre-drying Time: /
- Melting Temperature: /
- Mold Temperature: /
Note: All technical indicators above are provided for reference only and are not guaranteed values. Users must verify processing suitability according to specific application requirements.