PETG SD2012G
PRODUCT DETAILS
SD2012G Material Performance Description
SD2012G is a transparent engineering material produced by Su Master New Materials (Guangdong) Co., Ltd.. It delivers excellent optical clarity along with balanced rigidity and stable thermal performance, making it suitable for common injection molding applications requiring transparency and good dimensional stability.
✅ Key Physical, Mechanical & Optical Properties
| Property | Test Standard | Condition | Unit | SD2012G |
|---|---|---|---|---|
| Specific Gravity | GB/T 1033 | — | g/cm³ | 1.27 |
| Melt Index | GB/T 3682 | 230℃ / 3.8kg | g/10min | / |
| Tensile Strength | GB/T 1040 | 10mm/min | MPa | 30 |
| Elongation at Break | GB/T 6344 | 10mm/min | % | / |
| Flexural Strength | GB/T 9341 | 2mm/min | MPa | 64 |
| Flexural Modulus | GB/T 9341 | 2mm/min | MPa | 1800 |
| Izod Impact Strength (Notched) | GB/T 1843 | 1/8 inch | KJ/㎡ | 1.8 |
| Light Transmittance | GB/T 2410 | 3mm | T(C) | 90 |
| Haze | GB/T 2410 | 3mm | H(C) | 1 |
| Heat Deflection Temperature | GB/T 1634 | 1.8MPa | ℃ | 62 |
| Fire Rating | GB/T 2048 | mm / 1.5min | — | HB |
✅ Recommended Injection Molding Conditions
- Pre-drying Temperature: /
- Pre-drying Time: /
- Melting Temperature: /
- Mold Temperature: /
Note: All technical data listed above are for reference only and should not be regarded as guaranteed values. Users must test the material to ensure suitability for their actual process and application.