1111
PC+ABS SD3020H
PRODUCT DETAILS
SD3020H Material Performance Description
SD3020H is a high-performance engineering material developed by Su Master New Materials (Guangdong) Co., Ltd.. It delivers excellent toughness, high impact resistance, superior heat performance, and reliable V0 flame retardancy, making it ideal for advanced injection molding applications that require enhanced durability and safety.
✅ Key Physical & Mechanical Properties
| Property | Test Standard | Condition | Unit | SD3020H |
|---|---|---|---|---|
| Specific Gravity | GB/T 1033 | — | g/cm³ | 1.19 |
| Melt Index | GB/T 3682 | 230℃ / 3.8kg | g/10min | 10 |
| Tensile Strength | GB/T 1040 | 10mm/min | MPa | 55 |
| Elongation at Break | GB/T 6344 | 10mm/min | % | 80 |
| Flexural Strength | GB/T 9341 | 2mm/min | MPa | 90 |
| Flexural Modulus | GB/T 9341 | 2mm/min | MPa | 2200 |
| Izod Impact Strength (Notched) | GB/T 1843 | 1/8 inch | KJ/㎡ | 65 |
| Heat Deflection Temperature | GB/T 1634 | 1.8MPa | ℃ | 100 |
| Flame Rating | GB/T 2048 | mm / 1.5 min | — | V0 |
✅ Recommended Injection Molding Conditions
- Pre-drying Temperature: 90–95℃
- Pre-drying Time: 3 hours
- Melting Temperature: 270℃
- Mold Temperature: 90℃
Note: The above technical data are for reference only and should not be used as guaranteed values. Users must evaluate the suitability according to their specific application and processing requirements.